PHZF - Continuous Flat Heat Shrink

PHZF20024

• Diameter after shrinking

  1.2 mm
• Diameter before shrinking

  2.4 mm
• Shrink ratio

  2:1
• Thickness

  0.51 mm
• Working Temperature

  from -55 °C to 105 °C

PHZF20032

• Diameter after shrinking

  1.6 mm
• Diameter before shrinking

  3.2 mm
• Shrink ratio

  2:1
• Thickness

  0.51 mm
• Working Temperature

  from -55 °C to 105 °C

PHZF20048

• Diameter after shrinking

  2.4 mm
• Diameter before shrinking

  4.8 mm
• Shrink ratio

  2:1
• Thickness

  0.51 mm
• Working Temperature

  from -55 °C to 105 °C

PHZF20064

• Diameter after shrinking

  3.2 mm
• Diameter before shrinking

  6.4 mm
• Shrink ratio

  2:1
• Thickness

  0.64 mm
• Working Temperature

  from -55 °C to 105 °C

PHZF20095

• Diameter after shrinking

  4.8 mm
• Diameter before shrinking

  9.5 mm
• Shrink ratio

  2:1

PHZF20127

• Diameter after shrinking

  6.4 mm
• Diameter before shrinking

  12.7 mm
• Shrink ratio

  2:1
• Thickness

  0.64 mm
• Working Temperature

  from -55 °C to 105 °C

PHZF20190

• Diameter after shrinking

  9.5 mm
• Diameter before shrinking

  19 mm
• Shrink ratio

  2:1
• Thickness

  0.77 mm
• Working Temperature

  from -55 °C to 105 °C

PHZF20254

• Diameter after shrinking

  12.7 mm
• Diameter before shrinking

  25.4 mm
• Shrink ratio

  2:1
• Thickness

  0.89 mm
• Working Temperature

  from -55 °C to 105 °C

PHZF20380

• Diameter after shrinking

  19.1 mm
• Diameter before shrinking

  38 mm
• Shrink ratio

  2:1
• Thickness

  1.02 mm
• Working Temperature

  from -55 °C to 105 °C

PHZF20504

• Diameter after shrinking

  25.4 mm
• Diameter before shrinking

  50.4 mm
• Shrink ratio

  2:1
• Thickness

  0.97 mm
• Working Temperature

  from -55 °C to 105 °C

PHZF30024

• Diameter after shrinking

  0.8 mm
• Diameter before shrinking

  2.4 mm
• Shrink ratio

  3:1
• Thickness

  0.53 mm
• Working Temperature

  from -55 °C to 135 °C

PHZF30032

• Diameter after shrinking

  1 mm
• Diameter before shrinking

  3.2 mm
• Shrink ratio

  3:1
• Thickness

  0.58 mm
• Working Temperature

  from -55 °C to 135 °C

PHZF30048

• Diameter after shrinking

  1.6 mm
• Diameter before shrinking

  4.8 mm
• Shrink ratio

  3:1
• Thickness

  0.58 mm
• Working Temperature

  from -55 °C to 135 °C

PHZF30064

• Diameter after shrinking

  2 mm
• Diameter before shrinking

  6.4 mm
• Shrink ratio

  3:1
• Thickness

  0.63 mm
• Working Temperature

  from -55 °C to 135 °C

PHZF30095

• Diameter after shrinking

  3 mm
• Diameter before shrinking

  9.5 mm
• Shrink ratio

  3:1
• Thickness

  0.63 mm
• Working Temperature

  from -55 °C to 135 °C

PHZF30127

• Diameter after shrinking

  4 mm
• Diameter before shrinking

  12.7 mm
• Shrink ratio

  3:1
• Thickness

  0.68 mm
• Working Temperature

  from -55 °C to 135 °C

PHZF30191

• Diameter after shrinking

  6 mm
• Diameter before shrinking

  19.1 mm
• Shrink ratio

  3:1
• Thickness

  0.9 mm
• Working Temperature

  from -55 °C to 135 °C

PHZF30254

• Diameter after shrinking

  8 mm
• Diameter before shrinking

  25.4 mm
• Shrink ratio

  3:1
• Thickness

  1 mm
• Working Temperature

  from -55 °C to 135 °C

PHZF30381

• Diameter after shrinking

  12.7 mm
• Diameter before shrinking

  38.1 mm
• Shrink ratio

  3:1
• Thickness

  1.1 mm
• Working Temperature

  from -55 °C to 105 °C